| Features and main uses： | |||||
|
1.FH-123 is a kind of o-benzene unsaturated polyester solution in styrene, which has been added with accelerant and thixotropic agent. It has low viscosity, low reaction exothermic temperature and good construction performance. At the same time, it has excellent mechanical strength, which is suitable for FRP fishing boats, yachts, lifeboats and other large-scale molded products. |
|||||
| 2.It has been approved by China Classification Society. | |||||
| 3.FH-123 (N) W winter type, suitable for November to February (below 15 ℃) | |||||
| FH-123 (N) M spring autumn type, suitable for March to may, September to October (15 ~ 25 ℃) | |||||
| FH-123 (N) S summer type, suitable for June to August (above 25 ℃) | |||||
| FH-123W 、FH-123M、 FH-123S contains wax and has dry property | |||||
| FH-123NW 、FH-123NM、 FH-123NS No wax, non air dry | |||||
| Technical index of liquid resin: | |||||
| Project | Company | FH-123(N)W | FH-123(N)M | FH-123(N)S | Test Method |
| Viscosity（25℃） | Pa•s | 0.17~0.28 | 0.26~0.40 | 0.30~0.50 |
JIS K 6901 Butanox M-50：1.0% |
| Thixotropy index | ... | 2.0~3.4 | 2.0~3.4 | 2.0~3.4 | |
| Gel time（25℃） | min | 10.0~18.0 | 22.0~38.0 | 30.0~55.0 | |
| Physical properties of casting body: | |||||
| Project | Company | Measured value | Test Method | ||
| Tensile strength | MPa | 62.0 | JIS K 7113 | ||
| Tensile modulus of elasticity | MPa | 3900.0 | JIS K 7113 | ||
| Breaking extensibility | ... | 2.00% | JIS K 7113 | ||
| Bending strength | MPa | 120.0 | JIS K 7203 | ||
| Bending modulus of elasticity | MPa | 3800.0 | JIS K 7203 | ||
| Compressive strength | MPa | 137.0 | JIS K 7208 | ||
| Impact strength | KJ/m² | 21.0 | JIS K 7111 | ||
| Shrinkage | ... | 7.80% | ... | ||
| Hot deformation temperature | ℃ | 65 | JIS K 7207 | ||
| Barcol hardness | ... | 42 | JIS K 7209 | ||
| Moisture content | ... | 0.22% | JIS K 7060 | ||
| Note: 1. Dosage of curing agent:Butanox M-50 1.0% | |||||
| 2.Casting body: 3 mm thick, post curing: room temperature×24 hours + 110 ℃×2 hours. | |||||
| Matters needing attention: | |||||
| 1. Before use, please mix evenly in the packaging barrel, or pour out all the resin in the packaging barrel and stir it evenly before use. | |||||
| 2. The user should select the corresponding type of resin according to the specific environmental conditions and construction process requirements. | |||||
| 3. The product should be stored in a cool place below 25 ℃ to avoid fire and keep away from heat and radiation sources. The shelf life of products stored below 25 ℃ is 3 months. | |||||
| In view of the diversity of application conditions, it is necessary for users to confirm the product performance. If you have any questions about the contents of this information or want to know more information, please contact our company. We reserve the right to modify the data. | |||||