L0_TM-107M（新江-1)
|
Features and main uses：
|
|
TM-107M is a high activity reactive flame retardant unsaturated polyester resin. The resin has the advantages of pre promotion, good workability, anti sagging, good wettability to glass fiber and high mechanical strength. It is suitable for hand paste and RTM molding process. Tm-107m (Xinjiang-1) is suitable for manufacturing flame-retardant products such as ships, vehicles, cooling towers, buildings, cable boxes, underground parts of coal mines, etc.
|
|
Certification and flame retardant level：
|
|
China Classification Society (CCS): IMO MSC / cire.1006 fire resistant and flame retardant
|
|
|
|
Technical index of liquid resin（25℃）:
|
|
Project
|
Company
|
TM-107M(新江-1)（N）W
|
TM-107M(新江-1)（N）M
|
TM-107M(新江-1)（N）S
|
Test Method
|
|
Appearance
|
...
|
Light red turbid liquid
|
...
|
|
Viscosity
|
Pa•s
|
0.24~0.38
|
0.38~0.62
|
0.38~0.62
|
JIS K 6901.5.5.1
|
|
Thixotropy index
|
...
|
≥2.0
|
JIS K 6901.5.6
|
|
Gel time
|
min
|
10.0~18.0
|
15.0~25.0
|
40.0~55.0
|
GB/T7193.4.6-2008
|
|
Note: gel time test:Curing agent Butanox M-50 2.0%
|
|
|
|
Physical properties of casting body:
|
|
Project
|
Company
|
Measured value
|
Test Method
|
|
|
Tensile strength
|
MPa
|
55
|
GB/T 2568-1995
|
|
Tensile modulus of elasticity
|
MPa
|
2880
|
GB/T 2568-1995
|
|
Breaking extensibility
|
...
|
1.83%
|
GB/T 2568-1995
|
|
Bending strength
|
MPa
|
100.1
|
GB/T 2570-1995
|
|
Bending modulus of elasticity
|
MPa
|
3100
|
GB/T 2570-1995
|
|
Impact strength
|
KJ/M²
|
8.73
|
GB/T 2571-1995
|
|
Barcol hardness
|
...
|
40
|
GB/T 3854-2005
|
|
Hot deformation temperature
|
℃
|
65
|
GB/T 1634-2004
|
|
Oxygen index
|
...
|
23%
|
GB/T 2406-1993
|
|
Note: 1. The preparation method is in accordance with GB / T8237-2005，Curing system: Curing agent Butanox M-50 1.0%.
|
|
2. Casting body post-treatment: room temperature×24 hours + 60 ℃×3 hours + 80 ℃×2 hours.
|
|
|
|
Matters needing attention:
|
|
1. Mix the resin evenly before use.
|
|
2. When the construction environment humidity is high or the temperature is high, it is easy to cause the surface to become sticky. At this time, rs-102 wax can be properly added, and the recommended addition amount is 0.4 ~ 0.8%.
|
|
3. The product should be stored in a cool place below 25 ℃ to avoid fire and keep away from heat and radiation sources. The shelf life of products stored below 25 ℃ is 3 months.
|
|
|
|
|
|
|
|
|
In view of the diversity of application conditions, it is necessary for users to confirm the product performance. If you have any questions about the contents of this information or want to know more information, please contact our company. We reserve the right to modify the data.
|